Properties |
Aeroflex-Standard |
Test Method |
|
Cell Structure |
Closed Cell |
- |
|
Density lbs/ft3 (Kg/m3) |
2.5-5.0 (40-80)* |
ASTM D 1667 |
|
Thermal Conductivity |
Mean Temp |
-4oF |
32oF |
75oF |
90oF |
104oF |
ASTM C 177 |
|
BTU.in/ft2
hr
oF |
(-20oC) |
(0oC) |
(24oC) |
(32oC) |
(40oC) |
ASTM C 518 |
|
(W/ m.K) |
K-Value |
0.215 |
0.23 |
0.247 |
0.256 |
0.259 |
JIS A 1412 |
|
|
(0.0310) |
(0.0330) |
(0.0356) |
(0.0365) |
(0.0374) |
EN ISO 8497 |
|
Service Temperature |
-70 oF to 257
oF |
Becomes hard at -57oC
but can be used even at -200oC |
|
-57 oC to 125
oC |
|
Water Absorption |
< 10 (% by weight) |
ASTM D 1056 |
|
< 0.20 (% by volume) |
ASTM C 209 |
|
Water Vapor Permeability |
< 0.10 (1.44 x 10-10
g/Pa.s.m) |
ASTM E 96 |
|
perm.in (g/Pa.s.m) |
|
Ozone Resistance |
Very Good |
ASTM D 1149 |
|
ASTM D 1171 |
|
UV Weather Resistance |
Very Good |
ASTM G 154 |
|
Heat Stability (%Shrinkage) |
< 7% |
ASTM C 534 |
|
@ 220oF (104oC) x 7 days |
|
Flammability & Smoke Density |
Class V-0 |
UL 94 |
|
25/50 |
ASTM E 84 |
|
Self-Extinguishing |
ASTM D 635 |
|
Class 5.3 |
EMPA (Switzerland) |
|
Non-Flammable |
JIS K 6911 |
|
Pass |
IMO |
|
Mold Resistance |
|
Meet Requirement (Rating 1) |
UL 181 |
|
Fungi Resistance |
|
No Growth |
ASTM C1338 |
|
Bacteria Resistance |
|
Meet Requirement (Anti-Bacteria) |
ASTM E 2180 |
|
Corrosion of Copper/ Stainless Steel |
Non Corrosive |
DIN 1988 |
|
Nitrosamine Contents |
Not Detected |
FDA CPG 7117.11 |
|
RoHS |
Not Detected |
EN Restriction of the Use of Hazardous Substances Directive (RoHS) 2002/95/EC |
|
32 dB (20 mm) |
DIN EN ISO10052, DIN 4109-11 |
|
Flexibility |
Excellent |
ASTM C 534 |
|
Specifications
comply with ASTM C534-88.
* Figures show
the average values obtained by the world well-known testing institutes.
** Tested according
to DIN, JIS, ASTM and others.
*** Average
density of insulation thickness over 20 mm.
**** At temp.
under -57 °C AEROFLEX becomes hard,
but it does not affect thermal conductivity nor water vapor permeability.
In the heating applications AEROFLEX can stand +125 °C
continuously, and the adhesive up to +100 °C.
***** Water
vapor permeability tests were done under test method ASTM E96 dehydrate
test method at 37.8 °C.
****** IMO
: International Maritime Organization
******* It
is reported that Nitrosamin is harmful to human health even during storage.
No Nitrosamin compound was detected in AEROFLEX.
|